CERALENE® – LDPE waxes

CERALENE® types
for a broad range of industrial applications

Download Product overview

wax type:	LDPE
appearance:	white prills
acid number [mg KOH/g]:	0
drop point [°C]:	104
density at 23°C [g/cm3]:	0.92
viscosity (120°C) [mPa · s]:	240
penetration at 25°C [mm*10-¹]:	3
powder coatings:
masterbatch:	O
technical resins:
PVC:	+
wood/fibre-plastic composites:
bitumen:
hotmelt adhesive:
solvent based formulations:	++
water based additives:

wax type:	LDPE
appearance:	white prills
acid number [mg KOH/g]:	0
drop point [°C]:	102
density at 23°C [g/cm3]:	0.92
viscosity (120°C) [mPa · s]:	170
penetration at 25°C [mm*10-¹]:	4
powder coatings:	O
masterbatch:	O
technical resins:
PVC:	O
wood/fibre-plastic composites:
bitumen:	+
hotmelt adhesive:
solvent based formulations:	O
water based additives:

wax type:	LDPE
appearance:	white prills
acid number [mg KOH/g]:	0
drop point [°C]:	106
density at 23°C [g/cm3]:	0.92
viscosity (120°C) [mPa · s]:	550
penetration at 25°C [mm*10-¹]:	2
powder coatings:	+
masterbatch:	++
technical resins:
PVC:	++
wood/fibre-plastic composites:	++
bitumen:
hotmelt adhesive:
solvent based formulations:	+
water based additives:

wax type:	LDPE
appearance:	white prills
acid number [mg KOH/g]:	0
drop point [°C]:	109
density at 23°C [g/cm3]:	0.93
viscosity (120°C) [mPa · s]:	140
penetration at 25°C [mm*10-¹]:	3
powder coatings:
masterbatch:	O
technical resins:
PVC:	++
wood/fibre-plastic composites:
bitumen:
hotmelt adhesive:
solvent based formulations:
water based additives:

wax type:	LDPE
appearance:	white prills
acid number [mg KOH/g]:	0
drop point [°C]:	108
density at 23°C [g/cm3]:	0.92
viscosity (120°C) [mPa · s]:	850
penetration at 25°C [mm*10-¹]:	2
powder coatings:	++
masterbatch:	++
technical resins:	O
PVC:	+
wood/fibre-plastic composites:	++
bitumen:
hotmelt adhesive:
solvent based formulations:	O
water based additives:

wax type:	LDPE
appearance:	white prills
acid number [mg KOH/g]:	0
drop point [°C]:	109
density at 23°C [g/cm3]:	0.92
viscosity (120°C) [mPa · s]:	1100
penetration at 25°C [mm*10-¹]:	2
powder coatings:	++
masterbatch:	++
technical resins:	O
PVC:	+
wood/fibre-plastic composites:	++
bitumen:
hotmelt adhesive:
solvent based formulations:	O
water based additives:

wax type:	LDPE
appearance:	white prills
acid number [mg KOH/g]:	0
drop point [°C]:	101
density at 23°C [g/cm3]:	0.92
viscosity (120°C) [mPa · s]:	220
penetration at 25°C [mm*10-¹]:	3
powder coatings:
masterbatch:	++
technical resins:
PVC:	++
wood/fibre-plastic composites:
bitumen:
hotmelt adhesive:
solvent based formulations:	++
water based additives:

wax type:	LDPE
appearance:	white prills
acid number [mg KOH/g]:	0
drop point [°C]:	101
density at 23°C [g/cm3]:	0.92
viscosity (120°C) [mPa · s]:	320
penetration at 25°C [mm*10-¹]:	3
powder coatings:
masterbatch:	++
technical resins:
PVC:	++
wood/fibre-plastic composites:
bitumen:
hotmelt adhesive:
solvent based formulations:	++
water based additives:

O suitable + recommended ++ specially recommended

* at T=140 °C ** at T=150 °C *** at T=170 °C

¹⁾inks