CERALENE® – HDPE waxes

CERALENE® types
for a broad range of industrial applications

Download Product overview

wax type:	HDPE
appearance:	almost white prills
acid number [mg KOH/g]:	7-8
drop point [°C]:	121
density at 23°C [g/cm3]:	0.95
viscosity (120°C) [mPa · s]:	170
penetration at 25°C [mm*10-¹]:	1
powder coatings:	O
masterbatch:	+
technical resins:
PVC:
wood/fibre-plastic composites:	O
bitumen:	+
hotmelt adhesive:	+
solvent based formulations:	O
water based additives:	++

wax type:	HDPE
appearance:	almost white prills
acid number [mg KOH/g]:	0
drop point [°C]:	122
density at 23°C [g/cm3]:	0.96
viscosity (120°C) [mPa · s]:	400*
penetration at 25°C [mm*10-¹]:	< 1
powder coatings:
masterbatch:	O
technical resins:
PVC:	O
wood/fibre-plastic composites:
bitumen:	++
hotmelt adhesive:	+
solvent based formulations:
water based additives:

wax type:	HDPE
appearance:	almost white prills
acid number [mg KOH/g]:	0
drop point [°C]:	122
density at 23°C [g/cm3]:	0.96
viscosity (120°C) [mPa · s]:	200*
penetration at 25°C [mm*10-¹]:	< 1
powder coatings:
masterbatch:
technical resins:
PVC:	O
wood/fibre-plastic composites:
bitumen:	++
hotmelt adhesive:	+
solvent based formulations:
water based additives:

wax type:	HDPE
appearance:	almost white prills
acid number [mg KOH/g]:	0
drop point [°C]:	122
density at 23°C [g/cm3]:	0.96
viscosity (120°C) [mPa · s]:	800*
penetration at 25°C [mm*10-¹]:	< 1
powder coatings:
masterbatch:	+
technical resins:
PVC:	O
wood/fibre-plastic composites:
bitumen:	++
hotmelt adhesive:	+
solvent based formulations:
water based additives:

O suitable + recommended ++ specially recommended

* at T=140 °C ** at T=150 °C *** at T=170 °C

¹⁾inks