CERALENE® – LDPE waxes
CERALENE® types
for a broad range of industrial applications
CERALENE® 1M
| wax type: | LDPE |
|---|---|
| appearance: | white prills |
| acid number [mg KOH/g]: | 0 |
| drop point [°C]: | 104 |
| density at 23°C [g/cm3]: | 0.92 |
| viscosity (120°C) [mPa · s]: | 240 |
| penetration at 25°C [mm*10-¹]: | 3 |
| powder coatings: | |
| masterbatch: | O |
| technical resins: | |
| PVC: | + |
| wood/fibre-plastic composites: | |
| bitumen: | |
| hotmelt adhesive: | |
| solvent based formulations: | ++ |
| water based additives: |
CERALENE® 1X
| wax type: | LDPE |
|---|---|
| appearance: | white prills |
| acid number [mg KOH/g]: | 0 |
| drop point [°C]: | 102 |
| density at 23°C [g/cm3]: | 0.92 |
| viscosity (120°C) [mPa · s]: | 170 |
| penetration at 25°C [mm*10-¹]: | 4 |
| powder coatings: | O |
| masterbatch: | O |
| technical resins: | |
| PVC: | O |
| wood/fibre-plastic composites: | |
| bitumen: | + |
| hotmelt adhesive: | |
| solvent based formulations: | O |
| water based additives: |
CERALENE® 2E
| wax type: | LDPE |
|---|---|
| appearance: | white prills |
| acid number [mg KOH/g]: | 0 |
| drop point [°C]: | 106 |
| density at 23°C [g/cm3]: | 0.92 |
| viscosity (120°C) [mPa · s]: | 550 |
| penetration at 25°C [mm*10-¹]: | 2 |
| powder coatings: | + |
| masterbatch: | ++ |
| technical resins: | |
| PVC: | ++ |
| wood/fibre-plastic composites: | ++ |
| bitumen: | |
| hotmelt adhesive: | |
| solvent based formulations: | + |
| water based additives: |
CERALENE® 2G
| wax type: | LDPE |
|---|---|
| appearance: | white prills |
| acid number [mg KOH/g]: | 0 |
| drop point [°C]: | 109 |
| density at 23°C [g/cm3]: | 0.93 |
| viscosity (120°C) [mPa · s]: | 140 |
| penetration at 25°C [mm*10-¹]: | 3 |
| powder coatings: | |
| masterbatch: | O |
| technical resins: | |
| PVC: | ++ |
| wood/fibre-plastic composites: | |
| bitumen: | |
| hotmelt adhesive: | |
| solvent based formulations: | |
| water based additives: |
CERALENE® 2H
| wax type: | LDPE |
|---|---|
| appearance: | white prills |
| acid number [mg KOH/g]: | 0 |
| drop point [°C]: | 108 |
| density at 23°C [g/cm3]: | 0.92 |
| viscosity (120°C) [mPa · s]: | 850 |
| penetration at 25°C [mm*10-¹]: | 2 |
| powder coatings: | ++ |
| masterbatch: | ++ |
| technical resins: | O |
| PVC: | + |
| wood/fibre-plastic composites: | ++ |
| bitumen: | |
| hotmelt adhesive: | |
| solvent based formulations: | O |
| water based additives: |
CERALENE® 2T
| wax type: | LDPE |
|---|---|
| appearance: | white prills |
| acid number [mg KOH/g]: | 0 |
| drop point [°C]: | 109 |
| density at 23°C [g/cm3]: | 0.92 |
| viscosity (120°C) [mPa · s]: | 1100 |
| penetration at 25°C [mm*10-¹]: | 2 |
| powder coatings: | ++ |
| masterbatch: | ++ |
| technical resins: | O |
| PVC: | + |
| wood/fibre-plastic composites: | ++ |
| bitumen: | |
| hotmelt adhesive: | |
| solvent based formulations: | O |
| water based additives: |
CERALENE® 2V/220
| wax type: | LDPE |
|---|---|
| appearance: | white prills |
| acid number [mg KOH/g]: | 0 |
| drop point [°C]: | 101 |
| density at 23°C [g/cm3]: | 0.92 |
| viscosity (120°C) [mPa · s]: | 220 |
| penetration at 25°C [mm*10-¹]: | 3 |
| powder coatings: | |
| masterbatch: | ++ |
| technical resins: | |
| PVC: | ++ |
| wood/fibre-plastic composites: | |
| bitumen: | |
| hotmelt adhesive: | |
| solvent based formulations: | ++ |
| water based additives: |
CERALENE® 2V/320
| wax type: | LDPE |
|---|---|
| appearance: | white prills |
| acid number [mg KOH/g]: | 0 |
| drop point [°C]: | 101 |
| density at 23°C [g/cm3]: | 0.92 |
| viscosity (120°C) [mPa · s]: | 320 |
| penetration at 25°C [mm*10-¹]: | 3 |
| powder coatings: | |
| masterbatch: | ++ |
| technical resins: | |
| PVC: | ++ |
| wood/fibre-plastic composites: | |
| bitumen: | |
| hotmelt adhesive: | |
| solvent based formulations: | ++ |
| water based additives: |
O suitable + recommended ++ specially recommended
* at T=140 °C ** at T=150 °C *** at T=170 °C
1) inks